| 245 | 0 | _aStudy on the properties of natural rubber latex reinforced by polystyrene resin emulsion | |
| 260 |
_bProceedings of IRRDB Symposium 1999, Hainan, Peoples Republic of China. pp.437-450. _c1999 |
||
| 520 | _aThe effects of different preparation technology and proportion of PS to NR on the natural rubber latexs vulcanized rubber films mechanical properties, the reinforced NR latexs colloid property, rubber film-forming property and its vulcanized rubber films solvent resistance and ageing resistance were investigated. Relative Reinforced Degree (RRD) is characterized the reinforced effect of NR latex. The results show that: PS emulsion can reinforce NR latex effectively; The reinforced NR latex which uses in situ polymerizing technology overcomes thickening phenomenon which is very easy to be caused by pre-polymerizing and blending technology; the reinforced NR latex still have very good film-forming effect; the solvent resistance and ageing resistance of the reinforced vulcanized rubber film are improved, and the age-resisting property of the vulcanized rubber film using in situ polymerizing technology is worse than that of using pre-polymerizing and blending. The adherent way of PS resin R were studied by means of extraction. | ||
| 650 | _aEmulsion polymerization | ||
| 650 | _aNR latex | ||
| 650 | _aReinforcement | ||
| 650 | _aStyrene | ||